标题:Electrochemical preparation of NiAl intermetallic compound from solid oxides in molten CaCl2 and its corrosion behaviors in NaCl aqueous solution

作者:Yin, HY(Yin, Huayi);Yu, T(Yu, Tang);Tang, DY(Tang, Diyong);Ruan, XF(Ruan, Xuefeng);Zhu, H(Zhu, Hua);Wang, DH(Wang, Dihua)

来源出版物:MATERIALS CHEMISTRY AND PHYSICS 卷:133 期:1 页:465-470 出版年:MAR 15 2012

摘要:Nickel aluminide powders were prepared by direct electrochemical reduction of solid mixture of NiO-NiAl2O4 (Ni:Al = 1:1 in mol) precursor in molten CaCl2 at 850 degrees C. The reduction process of the solid oxide cathode was investigated by analyzing the intermediate products using X-ray diffraction (XRD) and scanning electron microscopy (SEM). It reveals that nickel is preferentially reduced and it benefits to prevent aluminum leaving from the cathode. The products obtained at the constant cell voltage electrolysis of 3.0 V for more than 4 h were stoichiometric NiAl. The energy consumption could be as low as 6.1 kWh (kg-NiAl)(-1) based on the applied cell voltage and the consumed electrolysis charge. Furthermore, the NiAl powders were made into a dense rod by spark plasma sintering (SPS) technique. The corrosion behaviors of the NiAl rod in 0.5 mol L-1 NaCl aqueous solution at room temperature were investigated by polarization curve and ac impedance measurements. It was found that the NiAl rod had satisfactory anti-corrosion ability in the solution. (C) 2012 Elsevier BM. All rights reserved.

文献类型:Article

语种:English

作者关键词:Corrosion test; Nickel aluminide; Electrochemical reduction; Molten salt

扩展关键词:ELECTROLYTIC REDUCTION; 3-PHASE INTERLINES; CALCIUM-CHLORIDE; INSULATOR COMPOUNDS; HYDROGEN-PRODUCTION; ALLOY; DECOMPOSITION; METHANE; MO; AL

通讯作者地址:Wang, DH (通讯作者),Wuhan Univ, Sch Resource & Environm Sci, Wuhan 430072, Peoples R China

地址:

[Yin, Huayi]Wuhan Univ, Sch Resource & Environm Sci, Wuhan 430072, Peoples R China

[Yu, Tang] Wuhan Univ, Sch Resource & Environm Sci, Wuhan 430072, Peoples R China

[Tang, Diyong] Wuhan Univ, Sch Resource & Environm Sci, Wuhan 430072, Peoples R China

[Ruan, Xuefeng] Wuhan Univ, Sch Resource & Environm Sci, Wuhan 430072, Peoples R China

[Zhu, Hua] Wuhan Univ, Sch Resource & Environm Sci, Wuhan 430072, Peoples R China

[Wang, Dihua] Wuhan Univ, Sch Resource & Environm Sci, Wuhan 430072, Peoples R China;Chinese Acad Sci, State Key Lab Corros & Protect, Inst Met Res, Shenyang 110016, Peoples R China

电子邮件地址:wangdh@whu.edu.cn"wangdh@whu.edu.cn

学科类别:Materials Science

ISSN: 0254-0584

信息服务
学院网站教师登录 学院办公电话 学校信息门户登录

版权所有 © 武汉大学资源与环境科学学院
地址:湖北省武汉市珞喻路129号 邮编:430079 
电话:027-68778381,68778284,68778296 传真:027-68778893