标题: Durability of platinum coating anode in molten carbonate electrolysis cell
作者: Du, KF (Du, Kaifa); Yu, R (Yu, Rui); Gao, MX (Gao, Muxing); Chen, ZG (Chen, Zhigang); Mao, XH (Mao, Xuhui); Zhu, H (Zhu, Hua); Wang, DH (Wang, Dihua)
来源出版物: CORROSION SCIENCE 卷: 153 页: 12-18 DOI: 10.1016/j.corsci.2019.03.028 出版年: JUN 2019
摘要: The performance and durability of a noble metal coating anode for oxygen evolution was investigated in molten Li2CO3-Na2CO3-K2CO3 at 450 degrees C for the first time. The consuming rate of Pt was evaluated to be below 4.1 x 10(-2) mm/a under anodic polarization by weight-loss and melt analysis measurements. The metallic substrate, titanium can be anodically passivated by forming a dense Li2TiO3 film in the melt. Platinum coated titanium (Pt/Ti) anode exhibited excellent durability within 100h electrolysis, but slight oxygen penetration under the coating was observed, which might lead to the failure of the material for much longer term application.
作者关键词: Platinum; Metal coatings; Molten salts; Polarization; Anodic dissolution; Oxidation
地址: [Du, Kaifa; Yu, Rui; Gao, Muxing; Chen, Zhigang; Mao, Xuhui; Zhu, Hua; Wang, Dihua] Wuhan Univ, Sch Resource & Environm Sci, Int Cooperat Base Sustainable Utilizat Resources, Wuhan 430072, Hubei, Peoples R China.
通讯作者地址: Wang, DH (通讯作者)，Wuhan Univ, Sch Resource & Environm Sci, Int Cooperat Base Sustainable Utilizat Resources, Wuhan 430072, Hubei, Peoples R China.
版权所有 © 武汉大学资源与环境科学学院