标题: Rearrangement of oxide scale on Ni-11Fe-10Cu alloy under anodic polarization in molten Na2CO3-K2CO3

作者: Cheng, XH (Cheng, Xinhua); Yin, HY (Yin, Huayi); Wang, DH (Wang, Dihua)

来源出版物:CORROSION SCIENCE  卷:141 页码: 168-174     DOI10.1016/j.corsci.2018.07.014       出版年: AUG 15 2018

摘要:The effect of anodic polarization on a pre-formed oxide scale of Ni-11Fe-10Cu alloy was investigated in Na2CO3K2CO3 melt at 750 degrees C. The pre-formed oxide scale rearranged under anodic polarization and enabled the alloy as an inert anode for oxygen evolution. The anodic polarization has a positive effect on repairing defects in the original oxide scale, i.e., repair-enhancement effect, which can enhance the protectivity of an alloy substrate and eliminate further corrosion and oxidation. This study demonstrates an effective way to prepare a protective oxide scale, and reveals the rearrangement of pre-formed oxide scale under anodic polarization.

入藏号:WOS:000441682000018

文献类型:Article

语种:English

作者关键词: Anodic oxidation; Inert anode; Molten salts; Oxide scale; Rearrangement

扩展关键词: HIGH-TEMPERATURE OXIDATION; TRANSITION-METAL OXIDES; CRYOLITE-ALUMINA MELTS; INERT ANODES; NICKEL FERRITE; PART I; CORROSION; CARBONATE; BEHAVIOR; OXYGEN

通讯作者地址:Wang, DH (reprint author), Wuhan Univ, Sch Resource & Environm Sci, Hubei Int Sci & Technol Cooperat Base Sustainable, Wuhan 430072, Hubei, Peoples R China.
Yin, HY (reprint author), Wuhan Univ, Sch Resource & Environm Sci, Wuhan 430072, Hubei, Peoples R China.

电子邮件地址:yinhy@smm.neu.edu.cn; wangdh@whu.edu.cn

地址:

[Cheng, Xinhua; Yin, Huayi; Wang, Dihua] Wuhan Univ, Sch Resource & Environm Sci, Hubei Int Sci & Technol Cooperat Base Sustainable, Wuhan 430072, Hubei, Peoples R China.
[Yin, Huayi] Northeastern Univ, Sch Met, Shenyang 110819, Liaoning, Peoples R China.

影响因子:4.862


信息服务
学院网站教师登录 学院办公电话 学校信息门户登录

版权所有 © 武汉大学资源与环境科学学院
地址:湖北省武汉市珞喻路129号 邮编:430079 
电话:027-68778381,68778284,68778296 传真:027-68778893     技术支持:尚网互联