博士生汤丁丁的论文在JOURNAL OF THE ELECTROCHEMICAL SOCIETY刊出
发布时间:2013-12-19 17:11:05     发布者:yz     浏览次数:

标题:Electrosynthesis of Ti2COn from TiO2/C Composite in Molten CaCl2: Effect of Electrolysis Voltage and Duration作者:Tang, Dingding; Xiao, Wei; Tian, Longfei; Wang, Dihua

来源出版物:JOURNAL OF THE ELECTROCHEMICAL SOCIETY 卷:160 期:11 页:F1192-F1196 DOI:10.1149/2.015311jes出版年:2013

摘要:Ti2COn powders with controllable oxygen contents have been successfully synthesized by electro-reduction of solid TiO2-graphite composite precursors in molten CaCl2. The effect of electrolysis time and applied cell voltage on the carbon and oxygen content of the product was systematically investigated. The reduction pathway of the composite electrode was studied based on the analysis of intermediate products using X-ray diffraction (XRD), scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS). It is suggested that the reduction starts with converting TiO2 and graphite to CaTiO3 and Ti2COn. The resulting CaTiO3 is then reduced to CaTi2O4 which is subsequently reduced to Ti2COn. The present graphite significantly accelerates the electro-reduction of TiO2. The oxygen content decreases with increasing the electrolysis cell voltage and prolonging the electrolysis time. It is found that the cell voltage and electrolysis duration should be strictly controlled to avoid oxygen-depletion in the final product. The obtained product shows good electronic conductivity at room temperature. This process exhibits a relatively high current efficiency for production of Ti2COn from TiO2-graphite composite. (C) 2013 The Electrochemical Society.

入藏号:WOS:000326905000079

文献类型:Article

语种:English

扩展关键词:TICXOY THIN-FILMS; FFC CAMBRIDGE PROCESS; TITANIUM OXYCARBIDE; CALCIUM-CHLORIDE; ELECTROCHEMICAL REDUCTION; CARBOTHERMAL SYNTHESIS; DEOXIDATION; DIOXIDE; PRECURSORS; POWDER

通讯作者地址:Tang, Dingding; Wuhan Univ, Sch Resource & Environm Sci, Wuhan 430072, Peoples R China.

电子邮件地址:wangdh@whu.edu.cn

地址:

[Tang, Dingding; Xiao, Wei; Tian, Longfei; Wang, Dihua]Wuhan Univ, Sch Resource & Environm Sci, Wuhan 430072, Peoples R China.

[Wang, Dihua] Chinese Acad Sci, Inst Met Res, State Key Lab Corros & Protect, Shenyang 110016, Peoples R China.

研究方向:Electrochemistry; Materials Science

ISSN:0013-4651

信息服务
学院网站教师登录 学院办公电话 学校信息门户登录

版权所有 © 武汉大学资源与环境科学学院
地址:湖北省武汉市珞喻路129号 邮编:430079 
电话:027-68778381,68778284,68778296 传真:027-68778893    邮箱:sres@whu.edu.cn