标题: Solidification of LiCl-Li2O oxide reduction salt into sodalite by a spark plasma sintering

作者: Jiang, YQ (Jiang, Yuqi); Gao, SB (Gao, Shuaibo); Li, P (Li, Peng); Ma, YS (Ma, Yongsong); Yin, HY (Yin, Huayi); Wang, DH (Wang, Dihua)

来源出版物: JOURNAL OF RADIOANALYTICAL AND NUCLEAR CHEMISTRY : 331 : 7 : 2919-2928 DOI: 10.1007/s10967-022-08376-0 提前访问日期: JUN 2022 出版年: JUL 2022

摘要: The waste LiCl-Li2O oxide reduction salt was solidified and transformed into sodalite by the spark plasma sintering method. Compared with traditional solidification method, SPS operates at a lower pressure, lower temperature, shorter processing time, and without sintering additive. The SPS-solidified sodalite presents a low porosity of 0.37% and low leaching rates of 2.21 g m(-2) d(-1) for Cs, 3.05 x 10(-1) g m(-2) d(-1) for Ba, and 3.12 x 10(-1) g m(-2) d(-1) for Sr. Overall, the SPS is a promising method to solidify various waste OR salts.

作者关键词: Sodalite; Spark plasma sintering; LiCl-Li2O salt; Solidification; Radioactive element

地址: [Jiang, Yuqi; Gao, Shuaibo; Li, Peng; Ma, Yongsong; Yin, Huayi; Wang, Dihua] Wuhan Univ, Sch Resource & Environm Sci, Hubei Int Sci & Technol Cooperat Base Sustainable, Wuhan 430072, Peoples R China.

通讯作者地址: Wang, DH (通讯作者)Wuhan Univ, Sch Resource & Environm Sci, Hubei Int Sci & Technol Cooperat Base Sustainable, Wuhan 430072, Peoples R China.

电子邮件地址: wangdh@whu.edu.cn

影响因子:1.754


信息服务
学院网站教师登录 学院办公电话 学校信息门户登录

版权所有 © 武汉大学资源与环境科学学院
地址:湖北省武汉市珞喻路129号 邮编:430079 
电话:027-68778381,68778284,68778296 传真:027-68778893    邮箱:sres@whu.edu.cn